Description
PROPERTIES | COMPONENT |
CHEMICAL BASE | PVC SOLVENT CEMENT |
CONSISTENCY | SYRUP |
DENSITY | » 0,981 + / – 0,04 g/ml |
VISCOSITY | » 20.000 cP |
SHORE-A HARDNESS | N.A. |
E-MODULUS AT 100 % | » 1,20 MPa (ISO 37) |
ELONGATION AT BREAK | N.A. |
SHEARING STRENGTH | N.A. |
SKIN FORMING TIME | » 2 – 4 min. (23°C & 50 % R.H.) |
CURING SPEED | » VERY FAST |
TEMPERATURE RESISTANCE | -40 / +80°C |
APPLICATION TEMPERATURE RANGE | +15 / +35°C |
COVERAGE | N.A. |
ACCESABILITY | 2 h |
CONFORM TO THE NORMS
|
ASTM D 2564 Standard
SCAQMD Rule 1168/316A PW-G/DWV/SW |