PU 2KE 06

PU 2KE 06
PU 2KE 06

PU 2KE 06 is a two-component FLEXIBLE polyurethane-based adhesive

Thixotropic only after mixing the two parts, odorless, black or natural color that polymerizes at room temperature, for the semi-structural bonding of a wide range of materials such as thermoplastics, steel, aluminum, cement, wood and glass.

FCA approved

Particularly suitable for quick bonding that should be able to flex not causing cracks inside the adhesive bead

  • Open time: 1 minute
  • Viscosity: 30.000 mPas (mixed parts)
  • Tensile strength: 8 N / mm2
  • Elongation at break: 190%
  • Hardness: 85 A
  • Color: Black -Translucent
  • Packaging: 50 ml – 400 ml – Drums

Attachment

TDS PU 2KE 06

Description

PROPERTIES COMPONENT A COMPONENT B
CHEMICAL NATURE Polyol MDI
COLOUR Black / Translucent Amber
APPEARANCE Liquid Liquid
DENSITY @ 25 °C 1,04 g/ml 1,20 g/ml
VISCOSITY @ 25 °C 5000 mPa.s 6000 mPa.s
MIXING RATIO BY VOLUME 1,00 1,00
MIXING RATIO BY WEIGHT 0,89 1,00
TYPICAL CHARACTERISTICS OF THE FINAL SYSTEM
COLOUR Black / Translucent
APPEARANCE Thixotropic
DENSITY 1,12 g/ml
VISCOSITY 30000 mPa.s
APPLICATION TEMPERATURE +10 / +30 °C
OPEN TIME (10 g @ 20°C) 1 min
FIXTURE TIME (10 g @ 20°C) 5 min
FULLY CURED TIME (10 g @ 20°C) 240 min
EXOTHERMIC PEAK OF REACTION 80 °C
HARDNESS 85 Shore A
MINIMUM GAP FILL 0,20 mm
TENSILE STRENGHT 8 N/mm2
ELONGATION AT BREAK 190 %
RESISTIVITY 1.2 x1013 Ωxcm
TEMPERATURE RESISTANCE – 40 / + 90 °C

Additional information

Specific work-setting (component)

DYNAMIC bonding-line > 100 cm (IMPACTS + VIBRATIONS + TORSIONS), Operating Temperature <0 ° C, STATIC bonding-line <100 cm (LIGHT HANDLING)
Type of joint (application mode)

BEAD – OVERLAP, SMALL POINT – DROP
Adhesive Working Time

< 1 MINUTE
Adhesive Fixture Time

< 1 MINUTE, < 10 MINUTES
Substrates (suitable adherings match))

CARBON FIBER-REINFORCED COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, GLASS REINFORCED FIBER COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS # CARBON FIBER-REINFORCED COMPOSITES, HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS # GLASS REINFORCED FIBER COMPOSITES, HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS # HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS, SEMI-FINISHED BUILDINGS # SEMI-FINISHED BUILDINGS, WOOD # GLASS REINFORCED FIBER COMPOSITES
component sector/process

AUTOMOTIVE – TRUCK – BUS – AGRICULTURAL, FORESTRY MACHINES, FOOD, INDUSTRIAL COMPONENTS, TRAINS
Type of failure mode (after joint stress)

ADHESIVE (bonding failure between adhesive and adhering: no residue on substrates)