PROPERTIES | PART A | PART B | MIXED PRODUCT |
COLOUR | White | Black | Dark Grey |
VISCOSITY @ 25 °C (Brookfield) | 50.000 – 80.000 Cps | 50.000 – 80.000 Cps | _ |
DENSITY @ 25 °C | 1,35 ± 0,05 g/cm3 | 1,7 ± 0,05 g/cm3 | 1,53 ± 0,05 g/cm3 |
OPEN TIME (5mm – 20°C) | _ | _ | 8 – 10 min. |
FIXTURE TIME (5mm – 20°C) | _ | _ | 20 – 25 min. |
MIXING RATIO BY WEIGHT | 100 | 121 | _ |
MIXING RATIO BY VOLUME | 100 | 100 | _ |
POLYMERIZED PRODUCT PROPERTIES | |
HARDNESS @ 25°C (ASTM D-676) | 65 – 75 Shore D |
SHRINKAGE | < 1 mm |
LAP SHEAR STRENGHT (ISO 4587)
1 Cycle: (60 min. @ 90°C + 7 days @ R.T. SMC/SMC Lam. cataphoresis / Lam. cataphoresis Lam. defatted / Lam. defatted |
18 MPa (Substrate failure) 8 MPa 10 MPa |
LAP SHEAR STRENGHT (ISO 4587)
1 Cycle: (10 min. @ 90°C + 30 min. @ 140°C + 90 min. @ 150 °C) SMC/SMC @ 23 °C SMC/SMC @ 80 °C |
13 MPa (Substrate failure) 6 MPa |
LAP SHEAR STRENGHT (ISO 4587)
3 Cycles: (8h @ -45°C + 8h @ +40°C in 98% R.H. + 4h @ -45°C) Galvanized Parts |
5,70 MPa |
THERMAL CONDUCTIVITY | 0,6 – 0,65 W/mK |
ADHERENCE (ACI 503R) | > 3,5 MPa |
EXOTHERMIC PEAK | 80 °C |
RESISTANCE TO THERMAL SHOCKS | -40 /+130 °C |
TENSILE ELONGATION (ASTM D-638, UNI EN ISO 527) | 25 – 35 % |