MK 10-03 is a FAST two-component polyurethane adhesive designed for the structural bonding of rigid plastic materials, ceramic materials, prepreg fibers.

  • High temperature resistance> 120 ° C
  • Thermosetting structural bonding> 15 MPa
  • Thixotropic and sandable
  • Hot modular reactivity
  • Low exothermic peak during hardening
  • Characterized by a very low shrinkage after hardening
  • Fair flexibility
  • Over-paintable
  • It can be used in various industrial sectors for bonding reinforced polyesters, ABS, polycarbonates and composite materials

FCA – Volkswagen approved


Attachment

TDS MK 10-03

Description

PROPERTIES PART A PART B MIXED PRODUCT
COLOUR Grey Off-White Grey
VISCOSITY @ 25 °C (Brookfield) 40.000 – 70.000 Cps 30.000 – 45.000 Cps _
DENSITY @ 25 °C 1,66 ± 0,05 g/cm3 1,17 ± 0,05 g/cm3 1,53 ± 0,05 g/cm3
OPEN TIME (5mm – 20°C) _ _ 03 – 10 min.
FIXTURE TIME (5mm – 20°C) _ _ 12 – 18 min.
MIXING RATIO BY WEIGHT 100 121 _
MIXING RATIO BY VOLUME 100 100 _
POLYMERIZED PRODUCT PROPERTIES
HARDNESS @ 25°C                                               (ASTM D-676) 55 – 73 Shore D
SHRINKAGE < 1 mm
LAP SHEAR STRENGHT  (ISO 4587)

1 Cycle: (60 min. @ 90°C + 7 days @ R.T.

SMC/SMC

Lam. cataphoresis / Lam. cataphoresis

Lam. defatted / Lam. defatted

  

 

18 MPa (Substrate failure)

8 MPa

10 MPa
LAP SHEAR STRENGHT  (ISO 4587)

1 Cycle: (10 min. @ 90°C + 30 min. @ 140°C + 90 min. @ 150 °C)

SMC/SMC @ 23 °C

SMC/SMC @ 80 °C

  

 

13 MPa (Substrate failure)

6 MPa
LAP SHEAR STRENGHT  (ISO 4587)

3 Cycles: (8h @ -45°C + 8h @ +40°C in 98% R.H. + 4h @ -45°C)

Galvanized Parts

  

 

5,70 MPa
THERMAL CONDUCTIVITY 0,6 – 0,65 W/mK
ADHERENCE  (ACI 503R) > 3,5 MPa
EXOTHERMIC PEAK 80 °C
RESISTANCE TO THERMAL SHOCKS -40 /+130 °C
TENSILE ELONGATION (ASTM D-638, UNI EN ISO 527) 25 – 35 %

Additional information

Specific work-setting (component)

DYNAMIC bonding-line > 100 cm (IMPACTS + VIBRATIONS + TORSIONS), Operating Temperature > 90 ° C, Operating Temperature <0 ° C, STATIC bonding-line <100 cm (LIGHT HANDLING)
Type of joint (application mode)

BEAD – OVERLAP
Adhesive Working Time

< 10 MINUTES
Adhesive Fixture Time

10 ÷ 30 MINUTES
Substrates (suitable adherings match))

CARBON FIBER-REINFORCED COMPOSITES # CARBON FIBER-REINFORCED COMPOSITES, CARBON FIBER-REINFORCED COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, GLASS REINFORCED FIBER COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS # CARBON FIBER-REINFORCED COMPOSITES, HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS # GLASS REINFORCED FIBER COMPOSITES, HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS # HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS, SEMI-FINISHED BUILDINGS # SEMI-FINISHED BUILDINGS, WOOD # GLASS REINFORCED FIBER COMPOSITES
component sector/process

AUTOMOTIVE – TRUCK – BUS – AGRICULTURAL, FORESTRY MACHINES, INDUSTRIAL COMPONENTS, MILITARY DEFENCE, SPORT, TRAINS
Type of failure mode (after joint stress)

ADHESIVE (bonding failure between adhesive and adhering: no residue on substrates), COHESIVE (bonding failure inside the adhesive: residue presence on substrates)