MK EP 600 UN

MK EP 600 UN is a two-component epoxy resin (resin + hardener) not loaded indicated for the bonding of different materials.

  • Mainly used for bonding metals (aluminum, steel, iron) and composite materials.
  • Suitable for the assembly of rigid plastics, marble, porcelain, ceramics, costume jewelery stones, hardwoods, glass and ferrite.
  • Rapid repair even at temperatures close to 0 °C.
  • Resistant to bases, diluted acids and poor to solvents.
  • Resistant to vibrations and shocks.
  • No shrinkage
  • Excellent adhesion on different substrates, without the use of specific surface primers
  • Liquid – self levelling

Attachment

TDS MK EP 600 UN

Description

PROPERTIES

 

 RESIN

(PART A)

 HARDENER

(PART B)
CHEMICAL NATURE Epoxy Resin Amine
COLOUR Whitish Amber
DENSITY at 25 °C 1,1 – 1,2 g/ml 0,93 – 1 g/ml
VISCOSITY at 25 °C 35.000 – 45.000 mPa.s 35.000 – 45.000 mPa.s
MIXING RATIO BY WEIGHT 100 80
MIXING RATIO BY VOLUME 100 100
TYPICAL CHARACTERISTICS OF THE MIXED PRODUCT
OPEN TIME at 25 °C ≈ 90 min.
FIXTURE TIME 300 min.
FULL CURE TIME 24 hours
EXOTHERMIC PEAK OF THE REACTION 80 °C
DENSITY 1,08 – 1,10 g/ml
HARDNESS > 80 Shore D
MINIMUM GAP FILL 0,50 mm
 

TENSILE STRENGHT (16h, 40°C)

(ISO 53283)

 

 Aluminium: 26 N/mm2

Steel: 25 N/mm2

Stainless steel: 22 N/mm2

Wood: 15 N/mm2

Ceramic: 15 N/mm2
ELONGATION AT BREAK < 10 %
TEMPERATURE RESISTANCE – 40 / + 75 °C
WATER RESISTANCE Good

Additional information

Specific work-setting (component)

Operating Temperature <0 ° C, STATIC bonding-line <100 cm (LIGHT HANDLING)
Type of joint (application mode)

≈ 100% of SURFACE, SMALL POINT – DROP
Substrates (suitable adherings match))

ARAMIDE FIBER-REINFORCED COMPOSITES # ARAMIDE FIBER-REINFORCED COMPOSITES, ARAMIDE FIBER-REINFORCED COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, ARAMIDE FIBER-REINFORCED COMPOSITES # METALS and/or ALLOYS (Al – Ti – Ni – Cr – Fe), CARBON FIBER-REINFORCED COMPOSITES # CARBON FIBER-REINFORCED COMPOSITES, CARBON FIBER-REINFORCED COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, CARBON FIBER-REINFORCED COMPOSITES # METALS and/or ALLOYS (Al – Ti – Ni – Cr – Fe), CARBON FIBER-REINFORCED COMPOSITES # METALS and/or ALLOYS (Cu / Zn – Fe – Pb), GLASS REINFORCED FIBER COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, GLASS REINFORCED FIBER COMPOSITES # METALS and / or ALLOYS (Cu / Zn – Fe – Pb), GLASS REINFORCED FIBER COMPOSITES # METALS and/or ALLOYS (Al – Ti – Ni – Cr – Fe), SEMI-FINISHED BUILDINGS # METALS and / or ALLOYS (Cu / Zn – Fe – Pb), SEMI-FINISHED BUILDINGS # SEMI-FINISHED BUILDINGS, WOOD # GLASS REINFORCED FIBER COMPOSITES, WOOD # WOOD
Adhesive Working Time

> 90 MINUTES, 30 ÷ 90 MINUTES
Adhesive Fixture Time

> 90 MINUTES, 30 ÷ 90 MINUTES
Type of failure mode (after joint stress)

COHESIVE (bonding failure inside the adhesive: residue presence on substrates), SUBSTRATE ((adhering structure failure: adhesive causes a fracture on substrate)
component sector/process

INDUSTRIAL COMPONENTS, NAUTICAL & NAVAL, SPORT, WIND ENERGY