MK EP 520

MK EP 520
MK EP 520 è una resina epossidica bi componente (resina + indurente)

MK EP 520 is a two-component epoxy resin (resin + hardener) not loaded indicated for the bonding of different materials.

Mainly used for bonding metals (aluminum, steel, iron) and composite materials.

  • Suitable for the assembly of rigid plastics, marble, porcelain, ceramics, costume jewelery stones, hard woods, glass and ferrite.
  • Average setting time
  • Rapid repair even at temperatures close to 0 ° C.
  • Solvets free
  • Resistant to bases, diluted acids and poor to solvents.
  • No shrinkage
  • Excellent adhesion on different substrates, without the use of specific surface primers

Attachment

TDS MK EP 520

Description

PROPRIETA’ RESINA INDURENTE
NATURA CHIMICA Resina Epossidica Mercaptano
COLORE Lattescente Ambra
DENSITA’ a 25 °C (ASTM D 1475) 1,14 – 1,18 g/ml 0,96 – 1,00 g/ml
VISCOSITA’ a 25 °C (EN13702-2) 10.000 – 20.000 mPa.s 10.000 – 20.000 mPa.s
RAPPORTO IN VOLUME 1 1
RAPPORTO IN PESO 1 0.8
CARATTERISTICHE TIPICHE DEL SISTEMA FINALE
TEMPO APERTO a 25 °C (40mm, 100ml) 30 – 40 minuti
TEMPO DI GELIFICAZIONE a 25°C (1mm) 4 – 5 ore
TEMPO DI FISSAGGIO (25 °C, 0,1mm) 5 – 7 ore
TEMPO DI INDURIMENTO FINALE (6mm, 25°C) 24 ore
DENSITA’ (25°C, ASTM D 792) 1,08 – 1,12 g/ml
DUREZZA (ASTM D 2240) 78 – 82 Shore D (24h)

81 – 85 Shore D (7gg)
GAP FILL FUNZIONALE MINIMO 0,50 mm
RESISTENZA AL TAGLIO PER TRAZIONE

(ASTM D 1002)

 Acciaio inox AISI 316, 7 gg TA     15,0 – 17,0 MPa

Acciaio inox AISI 316, 16h 40°C     14,5 – 16,0 MPa

Acciaio inox AISI 316, 3h 80°C     19,0 – 21,0 MPa

Alluminio, 7gg RT     17,0 – 19,0 MPa

Alluminio, 16h 40°C     17,5 – 19,5 MPa

Alluminio, 3h 80°C     22,0 – 24,0 MPa
RESISTENZA ALLA TEMPERATURA 100 – 105 °C massimo

Additional information

Specific work-setting (component)

Operating Temperature > 90 ° C, Operating Temperature <0 ° C, STATIC bonding-line <100 cm (LIGHT HANDLING)
Type of joint (application mode)

BEAD – OVERLAP
Substrates (suitable adherings match))

ARAMIDE FIBER-REINFORCED COMPOSITES # ARAMIDE FIBER-REINFORCED COMPOSITES, ARAMIDE FIBER-REINFORCED COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, ARAMIDE FIBER-REINFORCED COMPOSITES # METALS and/or ALLOYS (Al – Ti – Ni – Cr – Fe), CARBON FIBER-REINFORCED COMPOSITES # CARBON FIBER-REINFORCED COMPOSITES, CARBON FIBER-REINFORCED COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, CARBON FIBER-REINFORCED COMPOSITES # METALS and/or ALLOYS (Al – Ti – Ni – Cr – Fe), CARBON FIBER-REINFORCED COMPOSITES # METALS and/or ALLOYS (Cu / Zn – Fe – Pb), GLASS REINFORCED FIBER COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, GLASS REINFORCED FIBER COMPOSITES # METALS and / or ALLOYS (Cu / Zn – Fe – Pb), GLASS REINFORCED FIBER COMPOSITES # METALS and/or ALLOYS (Al – Ti – Ni – Cr – Fe), METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe) # METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe), METALS and / or ALLOYS (Cu / Zn – Fe – Pb) # METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe), METALS and / or ALLOYS (Cu / Zn – Fe – Pb) # METALS and / or ALLOYS (Cu / Zn – Fe – Pb), SEMI-FINISHED BUILDINGS # METALS and / or ALLOYS (Cu / Zn – Fe – Pb)
Adhesive Working Time

30 ÷ 90 MINUTES
Adhesive Fixture Time

> 90 MINUTES, 30 ÷ 90 MINUTES
Type of failure mode (after joint stress)

COHESIVE (bonding failure inside the adhesive: residue presence on substrates), SUBSTRATE ((adhering structure failure: adhesive causes a fracture on substrate)
component sector/process

AERONAUTICAL / AEROSPACE, AUTOMOTIVE – TRUCK – BUS – AGRICULTURAL, FORESTRY MACHINES, INDUSTRIAL COMPONENTS, MILITARY DEFENCE, SPORT