MK EP 500 R

MK EP 500 R is a two-component epoxy resin (resin + hardener) not loaded indicated for the bonding of different materials.

RAPID two-component epoxy resin (resin + hardener) not loaded indicated for the bonding of different materials.

  • Mainly used for bonding metals (aluminum, steel, iron) and composite materials
  • Suitable for the assembly of rigid plastics, marble, porcelain, ceramics, costume stones, hardwoods, glass and ferrite
  • Very fast setting
  • Rapid repair even at temperatures close to 0 °C
  • Solvents free
  • Resistant to bases, diluted acids and poor to solvents
  • No shrinkage
  • Excellent adhesion on different substrates, even without the use of specific surface primers

Attachment

MK_EP_500_R_ENG

Description

PROPERTIES RESIN HARDENER
CHEMICAL NATURE Epoxy Resin Mercaptan
COLOUR Straw Yellow Amber
DENSITY at 25 °C (ASTM D 1475) 1,15 – 1,19 g/ml 1,11 – 1,15 g/ml
VISCOSITY at 25 °C (EN13702-2) 6.000 – 8.000 mPa.s 10.000 – 18.000 mPa.s
VOLUME RATIO 1 1
TYPICAL CHARACTERISTICS OF THE MIXED PRODUCT
OPEN TIME @ 25 °C 3 – 4 minutes
POT LIFE 8 – 12 minutes
FIXTURE TIME 2 hours
FULL CURE TIME (6mm, 25°C) 24 hours
EXOTHERMIC PEAK OF THE REACTION 70 °C
DENSITY (ASTM D 792) 1,13 – 1,17 g/ml
HARDNESS (ASTM D 2240) 75 – 80 Shore D
MINIMUM GAP FILL 0,50 mm
TENSILE STRENGHT (Metal / Metal) 20 N/mm2
TENSILE ELONGATION < 10 %
TEMPERATURE RESISTANCE – 40 / + 70 °C
WATER RESISTANCE Good

 

Additional information

Specific work-setting (component)

Operating Temperature <0 ° C, STATIC bonding-line <100 cm (LIGHT HANDLING)
Type of joint (application mode)

BEAD – OVERLAP, SMALL POINT – DROP
Substrates (suitable adherings match))

ARAMIDE FIBER-REINFORCED COMPOSITES # ARAMIDE FIBER-REINFORCED COMPOSITES, ARAMIDE FIBER-REINFORCED COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, ARAMIDE FIBER-REINFORCED COMPOSITES # METALS and/or ALLOYS (Al – Ti – Ni – Cr – Fe), CARBON FIBER-REINFORCED COMPOSITES # CARBON FIBER-REINFORCED COMPOSITES, CARBON FIBER-REINFORCED COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, CARBON FIBER-REINFORCED COMPOSITES # METALS and/or ALLOYS (Al – Ti – Ni – Cr – Fe), CARBON FIBER-REINFORCED COMPOSITES # METALS and/or ALLOYS (Cu / Zn – Fe – Pb), GLASS # METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe), GLASS REINFORCED FIBER COMPOSITES # GLASS REINFORCED FIBER COMPOSITES, GLASS REINFORCED FIBER COMPOSITES # METALS and / or ALLOYS (Cu / Zn – Fe – Pb), GLASS REINFORCED FIBER COMPOSITES # METALS and/or ALLOYS (Al – Ti – Ni – Cr – Fe), METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe) # METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe), METALS and / or ALLOYS (Cu / Zn – Fe – Pb) # METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe), METALS and / or ALLOYS (Cu / Zn – Fe – Pb) # METALS and / or ALLOYS (Cu / Zn – Fe – Pb), SEMI-FINISHED BUILDINGS # METALS and / or ALLOYS (Cu / Zn – Fe – Pb)
Adhesive Working Time

< 10 MINUTES
Adhesive Fixture Time

< 10 MINUTES
Type of failure mode (after joint stress)

ADHESIVE (bonding failure between adhesive and adhering: no residue on substrates), COHESIVE (bonding failure inside the adhesive: residue presence on substrates), SUBSTRATE ((adhering structure failure: adhesive causes a fracture on substrate)
component sector/process

AUTOMOTIVE – TRUCK – BUS – AGRICULTURAL, FORESTRY MACHINES, INDUSTRIAL COMPONENTS, MILITARY DEFENCE, SPORT, TRAINS