| MK CA 46 is suitable to assemble difficult to bond materials that require a uniform distribution of the load and high resistance to loads and tensile/shear stresses. The product provides rapid bonding of a wide range of substrates, included metals, plastics and elastomers.
|
| Technology | Cyanoacrylate |
| Chemical nature | 2-alkoxy Ethyl CA |
| Appearance | Colourless liquid |
| Specific gravity (25°C) | 1,07 ± 0.02 g/cm3 |
| Viscosity (25°C)
(Cone & Plate) |
70 – 120 mPa.s |
| Characteristics | Anti “ring”, Low odor, not fumes |
| Typical substrate | Wood, paper, leather, fabric, ecc. |
| Specific work-setting (component) | Operating Temperature <0 ° C, STATIC bonding-line <100 cm (LIGHT HANDLING) |
|---|---|
| Type of joint (application mode) | HEAD to HEAD, SMALL POINT – DROP |
| Substrates (suitable adherings match)) | ELASTOMERS – GASKETS # ELASTOMERS – GASKETS, ELASTOMERS – GASKETS # METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe), FABRICS # ARAMIDE FIBER-REINFORCED COMPOSITES, FABRICS # CARBON FIBER-REINFORCED COMPOSITES, FABRICS # FABRICS, FABRICS # GLASS REINFORCED FIBER COMPOSITES, FABRICS # HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS, FABRICS # METALS and / or ALLOYS (Cu / Zn – Fe – Pb), HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS # HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS, LOW ENERGY SURFACE THERMO-PLASTIC POLYMERS # LOW ENERGY SURFACE THERMO-PLASTIC POLYMERS, LOW ENERGY SURFACE THERMO-PLASTIC POLYMERS # METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe), WOOD # WOOD |
| Adhesive Working Time | < 1 MINUTE |
| Adhesive Fixture Time | < 1 MINUTE, < 10 MINUTES |
| component sector/process | AERONAUTICAL / AEROSPACE, AUTOMOTIVE – TRUCK – BUS – AGRICULTURAL, FORESTRY MACHINES, INDUSTRIAL COMPONENTS, MILITARY DEFENCE, SPORT, TRAINS |
| Type of failure mode (after joint stress) | COHESIVE (bonding failure inside the adhesive: residue presence on substrates), SUBSTRATE ((adhering structure failure: adhesive causes a fracture on substrate) |