Description
Technology | Cyanoacrylate |
Chemical nature | Ethyl |
Appearance | Colourless liquid |
Specific gravity (25°C) | 1,06 ± 0.05 g/cm3 |
|
MK CA 200 is suitable to assemble difficult to bond materials that require a uniform distribution of the load and high resistance to loads and tensile/shear stresses. The product provides rapid bonding of a wide range of substrates, included metals, plastics and elastomers. |
Technology | Cyanoacrylate |
Chemical nature | Ethyl |
Appearance | Colourless liquid |
Specific gravity (25°C) | 1,06 ± 0.05 g/cm3 |
|
Specific work-setting (component) | Operating Temperature > 90 ° C, Operating Temperature <0 ° C, STATIC bonding-line <100 cm (LIGHT HANDLING) |
---|---|
Type of joint (application mode) | HEAD to HEAD, SMALL POINT – DROP |
Substrates (suitable adherings match)) | ELASTOMERS – GASKETS # ELASTOMERS – GASKETS, ELASTOMERS – GASKETS # METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe), FABRICS # ARAMIDE FIBER-REINFORCED COMPOSITES, FABRICS # CARBON FIBER-REINFORCED COMPOSITES, FABRICS # FABRICS, FABRICS # GLASS REINFORCED FIBER COMPOSITES, FABRICS # HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS, FABRICS # METALS and / or ALLOYS (Cu / Zn – Fe – Pb), HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS # HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS, LOW ENERGY SURFACE THERMO-PLASTIC POLYMERS # LOW ENERGY SURFACE THERMO-PLASTIC POLYMERS, LOW ENERGY SURFACE THERMO-PLASTIC POLYMERS # METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe), WOOD # WOOD |
Adhesive Working Time | < 1 MINUTE, < 10 MINUTES |
Adhesive Fixture Time | < 1 MINUTE, < 10 MINUTES |
component sector/process | AERONAUTICAL / AEROSPACE, AUTOMOTIVE – TRUCK – BUS – AGRICULTURAL, FORESTRY MACHINES, INDUSTRIAL COMPONENTS, MILITARY DEFENCE, SPORT, TRAINS |
Type of failure mode (after joint stress) | COHESIVE (bonding failure inside the adhesive: residue presence on substrates), SUBSTRATE ((adhering structure failure: adhesive causes a fracture on substrate) |