MK 2011

MK 2011 is a solvent-based polychloroprenic adhesive with low viscosity therefore suitable to be used with spray or brush.

Particularly suitable for bonding of foam rubber, polyurethane foam, leather, fabrics and similar.

Tipically it also used over metal, wood, concrete, plastic laminates, porous plastics.
Not suitable for surfaces exposed to UV rays through glass or crystal surfaces even for plastic materials with high plasticizer content.
The bonded materials remain elastic
Easy and quick application
Free from: Toluol.
Fair resistance to the temperature.
Good water resistance.
Excellent resistance to aging.
Spray-able.

Description

PROPERTIES	VALUES
CHEMICAL NATURE	POLYCHLOROPRENE AND MIXTURE OF RESINS
DENSITY	» 0,84 ± 0,05 g/ml
VISCOSITY (Ford Cup n. 4)	1,40 – 2 min
COLOUR	STRAW YELLOW
SOLID CONTENT	16 – 20 %
TACK FREE TIME	15 – 20 min. on standard conditions
OPEN TIME	≈ 30 min.
MAXIMUM STRENGHT TIME	After 24 – 48 hours
INITIAL GRIP	STRONG
WATER RESISTANCE	GOOD
TEMPERATURE RESISTANCE	-40 / +70 °C
APPLICATION TEMPERATURE	+15 / +30°C

Type of joint (application mode)	≈ 100% of SURFACE
Type of failure mode (after joint stress)	ADHESIVE (bonding failure between adhesive and adhering: no residue on substrates), COHESIVE (bonding failure inside the adhesive: residue presence on substrates)
Specific work-setting (component)	Operating Temperature <0 ° C, STATIC bonding-line <100 cm (LIGHT HANDLING)
Substrates (suitable adherings match))	FABRICS # ARAMIDE FIBER-REINFORCED COMPOSITES, FABRICS # CARBON FIBER-REINFORCED COMPOSITES, FABRICS # FABRICS, FABRICS # GLASS REINFORCED FIBER COMPOSITES, FABRICS # HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS, FABRICS # METALS and / or ALLOYS (Cu / Zn – Fe – Pb), WOOD # WOOD
Adhesive Working Time	< 10 MINUTES
Adhesive Fixture Time	10 ÷ 30 MINUTES
component sector/process	AUTOMOTIVE – TRUCK – BUS – AGRICULTURAL, FORESTRY MACHINES, INDUSTRIAL COMPONENTS, NAUTICAL & NAVAL, TRAINS