Contact polychloroprene solvent based adhesive indicated for bonding leather, wood, metal, rubber ..
| PROPRIETA’ | VALORI |
| NATURA CHIMICA | POLICLOROPRENE E RESINE IN MISCELA |
| DENSITA’ | » 0,88 ± 0,05 g/ml |
| VISCOSITA’ | 10.000 ± 2.000 mPa.s |
| COLORE | GIALLO PAGLIERINO |
| RESIDUO SECCO | ≈ 24 ± 1% |
| TEMPO DI ASCIUGATURA | 10 – 15 min. in condizioni normali |
| TEMPO APERTO | ≈ 30 min. |
| MASSIMA RESISTENZA | Dopo 24 – 48 ore |
| RESA | 200 / 400 g/m² (a seconda del tipo di superficie) |
| RESISTENZA ALLA TEMPERATURA | -40 / +95 °C |
| TEMPERATURA DI APPLICAZIONE | +15 / +30°C |
| Type of joint (application mode) | ≈ 100% of SURFACE |
|---|---|
| Specific work-setting (component) | Operating Temperature > 90 ° C, Operating Temperature <0 ° C, STATIC bonding-line <100 cm (LIGHT HANDLING) |
| Substrates (suitable adherings match)) | FABRICS # ARAMIDE FIBER-REINFORCED COMPOSITES, FABRICS # CARBON FIBER-REINFORCED COMPOSITES, FABRICS # FABRICS, FABRICS # GLASS REINFORCED FIBER COMPOSITES, FABRICS # HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS, FABRICS # METALS and / or ALLOYS (Cu / Zn – Fe – Pb), WOOD # WOOD |
| Adhesive Working Time | < 10 MINUTES |
| Type of failure mode (after joint stress) | ADHESIVE (bonding failure between adhesive and adhering: no residue on substrates), COHESIVE (bonding failure inside the adhesive: residue presence on substrates) |
| Adhesive Fixture Time | 10 ÷ 30 MINUTES, 30 ÷ 90 MINUTES |
| component sector/process | AUTOMOTIVE – TRUCK – BUS – AGRICULTURAL, FORESTRY MACHINES, INDUSTRIAL COMPONENTS, NAUTICAL & NAVAL, SPORT, TRAINS |