MASTIKGRIP 9810

MASTIKGRIP 9810
MASTIKGRIP 9810
MASTIKGRIP 9810 - Tenacious hot-melt, solvent-free reactive polyurethane, heat-applicable

Tenacious hot-melt, solvent-free reactive polyurethane, heat-applicable.

  • Suitable for bonding: wood, fabrics, leather and plastics such as PVC – ABS ..
  • Particularly suitable in case of metals, glass, leather or when a particular water resistance is required.
  • Used for fast small assembly operations of motor vehicle components.
  • Excellent stability.
  • Excellent adhesion on different substrates, primerless.
  • Reduction of cleaning times.
  • Particularly useful for special bonding shoes parts.

Color: translucent
Open time: 45 – 75 sec.
Application temperature: 150 – 160 ° C
Viscosity: 7000 mPas


Attachment

TDS MASTIKGRIP 9810

Description

PROPERTIES VALUES
CHEMICAL NATURE HOT MELT REACTIVE POLYURETHANE
DENSITY 1,05 ± 0,05 g/ml
BROOKFIELD VISCOSITY at 120°C

(spindle 27–2,5 rpm)

 ≈ 7.000 mPa.s
COLOUR OFF WHITE
SOLID CONTENT ≈ 100 %
OPEN TIME (3 mm thickness at 20 °C) 45 – 75 sec.
CURE TIME from 48 to 72 hours
RING AND BALL < 95 °C
APPLICATION TEMPERATURE max 130 °C

Additional information

Specific work-setting (component)

Operating Temperature <0 ° C, STATIC bonding-line <100 cm (LIGHT HANDLING)
Type of joint (application mode)

BEAD – OVERLAP, SMALL POINT – DROP
Substrates (suitable adherings match))

GLASS # METALS and / or ALLOYS (Al – Ti – Ni – Cr – Fe), HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS # HIGH ENERGY SURFACE THERMO-PLASTIC POLYMERS, WOOD # WOOD
Adhesive Working Time

< 1 MINUTE
Adhesive Fixture Time

< 10 MINUTES
component sector/process

AUTOMOTIVE – TRUCK – BUS – AGRICULTURAL, FORESTRY MACHINES, INDUSTRIAL COMPONENTS, SPORT
Type of failure mode (after joint stress)

ADHESIVE (bonding failure between adhesive and adhering: no residue on substrates)